Structures by: Rial C.
Total: 30
Lanthanum calcium copper oxide (1.97/0.03/1/4)
Ca0.03CuLa1.97O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3513(1)Å b=5.3907(1)Å c=13.1603(3)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.95/0.05/1/4)
Ca0.05CuLa1.95O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3490(1)Å b=5.3822(1)Å c=13.1638(2)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.9/0.1/1/4)
Ca0.1CuLa1.9O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3440(1)Å b=5.3580(1)Å c=13.1752(2)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.88/0.12/1/4)
Ca0.12CuLa1.88O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3491(1)Å b=5.3491(1)Å c=13.1846(3)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.97/0.03/1/4)
Ca0.03CuLa1.97O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3336(3)Å b=5.4000(3)Å c=13.1256(6)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.95/0.05/1/4)
Ca0.05CuLa1.95O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3291(4)Å b=5.3946(4)Å c=13.1282(9)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.92/0.08/1/4)
Ca0.08CuLa1.92O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3271(3)Å b=5.3793(3)Å c=13.1327(6)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.9/0.1/1/4)
Ca0.1CuLa1.9O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3239(2)Å b=5.3709(2)Å c=13.1446(6)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.88/0.12/1/4)
Ca0.12CuLa1.88O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3304(3)Å b=5.3663(3)Å c=13.1464(7)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.97/0.03/1/4.09)
Ca0.03CuLa1.97O4.091
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3510(2)Å b=5.3801(2)Å c=13.1940(5)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.95/0.05/1/4.09)
Ca0.05CuLa1.95O4.09
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3514(2)Å b=5.3730(2)Å c=13.1945(5)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.92/0.08/1/4.08)
Ca0.08CuLa1.92O4.079
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3508(3)Å b=5.3640(3)Å c=13.1925(5)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.9/0.1/1/4.058)
Ca0.1CuLa1.9O4.058
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3474(2)Å b=5.3581(2)Å c=13.1870(3)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.88/0.12/1/4.058)
Ca0.12CuLa1.88O4.058
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.34975(9)Å b=5.34975(9)Å c=13.1874(2)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.97/0.03/1/4.12)
Ca0.03CuLa1.97O4.12
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3299(3)Å b=5.3870(3)Å c=13.1614(6)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.95/0.05/1/4.1)
Ca0.05CuLa1.95O4.1
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3310(3)Å b=5.3826(3)Å c=13.1623(6)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.92/0.08/1/4.07)
Ca0.08CuLa1.92O4.07
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3360(3)Å b=5.3671(3)Å c=13.1638(7)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.9/0.1/1/4.05)
Ca0.1CuLa1.9O4.05
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3311(3)Å b=5.3653(3)Å c=13.1570(5)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.88/0.12/1/4.05)
Ca0.12CuLa1.88O4.05
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3313(3)Å b=5.3666(3)Å c=13.1531(6)Å
α=90° β=90° γ=90°
Lanthanum calcium copper oxide (1.92/0.08/1/4)
Ca0.08CuLa1.92O4
Physica C (Amsterdam) (152,1988-) (1998) 297, 277-293
a=5.3456(1)Å b=5.3673(1)Å c=13.1698(3)Å
α=90° β=90° γ=90°
Ca0.1CuLa1.9O3.99
Ca0.1CuLa1.9O3.99
Physica C (1998) 297, 277-293
a=5.3239Å b=5.3709Å c=13.1446Å
α=90° β=90° γ=90°
Ca0.12CuLa1.88O3.99
Ca0.12CuLa1.88O3.99
Physica C (1998) 297, 277-293
a=5.3304Å b=5.3663Å c=13.1464Å
α=90° β=90° γ=90°
Ca0.05CuLa1.95O4.08
Ca0.05CuLa1.95O4.08
Physica C (1998) 297, 277-293
a=5.3310Å b=5.3826Å c=13.1623Å
α=90° β=90° γ=90°
Ca0.03CuLa1.97O4.1
Ca0.03CuLa1.97O4.1
Physica C (1998) 297, 277-293
a=5.3299Å b=5.3870Å c=13.1614Å
α=90° β=90° γ=90°
Ca0.03CuLa1.97O3.99
Ca0.03CuLa1.97O3.99
Physica C (1998) 297, 277-293
a=5.3336Å b=5.4000Å c=13.1256Å
α=90° β=90° γ=90°
Ca0.08CuLa1.92O3.99
Ca0.08CuLa1.92O3.99
Physica C (1998) 297, 277-293
a=5.3271Å b=5.3793Å c=13.1327Å
α=90° β=90° γ=90°
Ca0.03CuLa1.97O3.99
Ca0.03CuLa1.97O3.99
Physica C (1998) 297, 277-293
a=5.3513Å b=5.3907Å c=13.1603Å
α=90° β=90° γ=90°
Ca0.12CuLa1.88O3.914
Ca0.12CuLa1.88O3.914
Physica C (1998) 297, 277-293
a=5.34975Å b=5.34975Å c=13.1874Å
α=90° β=90° γ=90°
Ca0.05CuLa1.95O4.07
Ca0.05CuLa1.95O4.07
Physica C (1998) 297, 277-293
a=5.3514Å b=5.3730Å c=13.1945Å
α=90° β=90° γ=90°
Ca0.08CuLa1.92O4.069
Ca0.08CuLa1.92O4.069
Physica C (1998) 297, 277-293
a=5.3508Å b=5.3640Å c=13.1925Å
α=90° β=90° γ=90°